If a leather article such as a shoe or a glove were left next to a heater for an extended period of time, would the finish remain soft and flexible or would it change color and develop cracks within the leather finish? A new ASTM International standard will help to answer that question, giving manufacturers a clear method to predict and prevent such problems. ASTM D7912 , Test Method for…, Technical Contact:, Kadir Donmez, Leather Research Laboratory, University of Cincinnati, Cincinnati, Ohio, Phone: 513-242-6300; donmezk@uc.edu, ASTM Staff Contact:, Ashley Wiand, Phone: 610-832-9551; awiand@astm.org, ASTM PR Contact:, Barbara Schindler, Phone: 610-832-9603; bschindl@astm.org Release #9623
-
Recent changes in technology are now covered in a significant ASTM International standard used to measure the particle size of metal powders. The standard, ASTM B330 , Test Methods for Estimating Average Particle Size of Metal Powders and Related Compounds Using Air Permeability, is under the jurisdiction of Subcommittee B09.03 on Refractory Metal Powders , part of ASTM International Committee…, ASTM Committee B09 Next Meeting:, April 14-16, 2014, Hollywood, Fla., Technical Contact:, Frank Venskytis, Clayton, N.C., Phone: 919-553-8050; fvastm@embarqmail.com , ASTM Staff Contact:, Katerina Koperna, Phone: 610-832-9728; kkoperna@astm.org, ASTM PR Contact:, Barbara Schindler, Phone: 610-832-9603; bschindl@astm.org Release #9544
-
Wet blue and wet white are intermediate products used by tanneries that process natural hides and skins into leather. Natural fats and oils need to be largely removed from wet blue and wet white for leather processing to be done properly, but no standard had previously existed to evaluate the effectiveness of such removal. ASTM International Committee D31 on Leather has now developed such a…
-
Flow characteristics of fine metal powders are important in filling dies for pressing of powder metallurgy compacts, which are later sintered and sometimes machined into finished parts. The flow rate, as measured by a new ASTM standard, determines the flow necessary for a precise quantity of powder to be introduced into the die. The new standard, B964 , Test Methods for Flow Rate of Metal Powders…
-
Two recently approved ASTM International standards provide user-friendly tests for properties of sintered metallurgy products. The new standards, developed by Subcommittee B09.04 on Bearings, are ASTM B962 , Test Methods for Density of Compacted or Sintered Power Metallurgy (PM) Products Using Archimedes’ Principle, and ASTM B963 , Test Methods for Oil Content, Oil-Impregnation Efficiency and…
-
A proposed new standard being developed by ASTM International Committee B09 on Metal Powders and Metal Powder Products offers a solution to the challenge of handling and characterizing very fine powders. Subcommittee B09.02 on Base Metal Powders is developing the proposed standard, WK13023 , Test Method for Determination of Tap Density of Metallic Powders by a Constant Volume Measuring Method. …
-
Conventionally processed powder metallurgy materials often exhibit open microporosity at the surface. While it is a natural part of the process, this microporosity can affect the measurement of surface finishes. To cover this and other issues that arise from measuring the surface finish of powder metallurgy, ASTM International Committee B09 on Metal Powders and Metal Powder Products has developed…
-
ASTM International Committee D31 on Leather has decided to reactivate Subcommittee D31.05 on Upholstery. During a period of inactivity for several years, the subcommittee was combined with Subcommittee D31.04 on Apparel. However, the last two years have seen an increase in the level of participation from people involved in upholstery leather manufacturing, so the subcommittees have again been…